Kryptanate 100 Flex polyaspartic resin

Kryptanate 100 Flex is a polyaspartic varnish whose working time falls between standard polyurea-based systems and polyurethane-based systems. Extending the working time of the ready-mix mixture to up to 25 minutes at room temperature allows for manual application. As a solvent-free product, it allows for thicker layers, up to 500 g/m² ^, applied in a single coat. Curing time is significantly shorter than with traditional polyurethane-based varnishes. Additionally, Kryptanate 100 Flex can be used to seal colored sands.

Kryptanate 100 Flex – properties:

• Excellent resistance: Kryptanate 100 Flex is highly resistant to a wide range of chemicals, such as traditional fuels, aviation fuel, and concentrated alkalis. This resistance allows it to be used without any restrictions, including in garages. A complete chemical resistance table can be found in the product data sheet. Additionally, it has excellent resistance to weather and temperature conditions, making it suitable for use in refrigerated storage.
• Speed ​​of application: thanks to rapid polymerization, the applied coating is dry to the touch after just 75 minutes at 21 ^° C! It's worth mentioning that Kryptanate 100 Flex can be applied in layers ranging from 200 to 500 g/m² ^, significantly reducing renovation time.
• UV resistance: due to the aliphatic structure of the resin, the finished product is resistant to UV rays and weather conditions, which translates into no yellowing effect.
• Cleanliness: easy to keep clean with traditional water washing.

Kryptanate 100 Flex application:

• Industrial floors;
• Home garages;
• Bathrooms;
• Terraces;
• Public buildings.

Preparation of the substrate

1. Substrate requirements:

• The substrate should have a minimum tensile strength of 1.5 MPA and a minimum compressive strength of 25 MPA;
• Clean, free from water and other contaminants;
• Permissible humidity – up to 4%;
• The ideal substrate temperature during application should be between 10 ^o C and 25 ^o C;
• If higher moisture levels are suspected deep within the substrate, it is necessary to use an appropriate primer;
• Fresh concrete substrates should be cured for at least 3 weeks.
• The substrate should be absorbent and have a slightly rough structure, which will increase the adhesion of the finished product.

Preparation of Kryptanate 100 Flex:

• Kryptanate 100 Flex is available in two variants: 4 kg and 11 kg.
• In the first step, mix component A using a low-speed mixer, being careful not to incorporate air into the product. This will allow the fillers to dissolve completely.
• Next, measure the appropriate amount of component A into another container to prepare the finished product in a quantity that can be applied within the pot life of the mixture. Next, add the appropriate amount of component B. Mix again with a low-speed mixer for approximately 2 minutes. It is recommended to prepare the finished mixture for approximately 15 minutes of work to reduce potential losses resulting from the end of the pot life.

Kryptanate 100 Flex Application:

• The prepared Kryptanate 100 Flex mixture can be applied with a roller or brush from 200 g/m2 to 500 g/m2 in one layer on a previously prepared substrate.
• For safety reasons, airless spraying is not recommended.